Names | |
---|---|
IUPAC names
Manganese dioxide
Manganese(IV) oxide | |
Other names
Pyrolusite, hyperoxide of manganese, black oxide of manganese, manganic oxide
| |
Identifiers | |
3D model (
JSmol)
|
|
ChEBI | |
ChemSpider | |
ECHA InfoCard | 100.013.821 |
EC Number |
|
PubChem
CID
|
|
RTECS number |
|
UNII | |
CompTox Dashboard (
EPA)
|
|
| |
| |
Properties | |
MnO 2 | |
Molar mass | 86.9368 g/mol |
Appearance | Brown-black solid |
Density | 5.026 g/cm3 |
Melting point | 535 °C (995 °F; 808 K) (decomposes) |
Insoluble | |
+2280.0×10−6 cm3/mol [1] | |
Structure [2] | |
Tetragonal, tP6, No. 136 | |
P42/mnm | |
a = 0.44008 nm, b = 0.44008 nm, c = 0.28745 nm
| |
Formula units (Z)
|
2 |
Thermochemistry [3] | |
Heat capacity (C)
|
54.1 J·mol−1·K−1 |
Std molar
entropy (S⦵298) |
53.1 J·mol−1·K−1 |
Std enthalpy of
formation (ΔfH⦵298) |
−520.0 kJ·mol−1 |
Gibbs free energy (ΔfG⦵)
|
−465.1 kJ·mol−1 |
Hazards | |
GHS labelling: | |
Warning | |
H302, H332 | |
P261, P264, P270, P271, P301+P312, P304+P312, P304+P340, P312, P330, P501 | |
NFPA 704 (fire diamond) | |
Flash point | 535 °C (995 °F; 808 K) |
Safety data sheet (SDS) | ICSC 0175 |
Related compounds | |
Other
anions
|
Manganese disulfide |
Other
cations
|
Technetium dioxide Rhenium dioxide |
Manganese(II) oxide Manganese(II,III) oxide Manganese(III) oxide Manganese heptoxide | |
Except where otherwise noted, data are given for materials in their
standard state (at 25 °C [77 °F], 100 kPa).
|
Manganese dioxide is the
inorganic compound with the
formula MnO
2. This blackish or brown solid occurs naturally as the mineral
pyrolusite, which is the main ore of
manganese and a component of
manganese nodules. The principal use for MnO
2 is for dry-cell
batteries, such as the
alkaline battery and the
zinc–carbon battery.
[4] MnO
2 is also used as a
pigment and as a precursor to other manganese compounds, such as
KMnO
4. It is used as a
reagent in
organic synthesis, for example, for the oxidation of
allylic
alcohols. MnO
2 has an α-
polymorph that can incorporate a variety of atoms (as well as water molecules) in the "tunnels" or "channels" between the manganese oxide octahedra. There is considerable interest in α-MnO
2 as a possible cathode for
lithium-ion batteries.
[5]
[6]
Several
polymorphs of MnO
2 are claimed, as well as a hydrated form. Like many other dioxides, MnO
2 crystallizes in the
rutile
crystal structure (this polymorph is called
pyrolusite or β-MnO
2), with three-coordinate oxide anions and octahedral metal centres.
[4] MnO
2 is characteristically
nonstoichiometric, being deficient in oxygen. The complicated
solid-state chemistry of this material is relevant to the lore of "freshly prepared" MnO
2 in
organic synthesis.
[7] The α-polymorph of MnO
2 has a very open structure with "channels", which can accommodate metal ions such as silver or barium. α-MnO
2 is often called
hollandite, after a closely related mineral.
Naturally occurring manganese dioxide contains impurities and a considerable amount of manganese(III) oxide. Production of batteries and ferrite (two of the primary uses of manganese dioxide) requires high purity manganese dioxide. Batteries require "electrolytic manganese dioxide" while ferrites require "chemical manganese dioxide". [8]
One method starts with natural manganese dioxide and converts it using
dinitrogen tetroxide and water to a
manganese(II) nitrate solution. Evaporation of the water leaves the crystalline nitrate salt. At temperatures of 400 °C, the salt decomposes, releasing N
2O
4 and leaving a residue of purified manganese dioxide.
[8] These two steps can be summarized as:
In another process, manganese dioxide is
carbothermically reduced to
manganese(II) oxide which is dissolved in
sulfuric acid. The filtered solution is treated with
ammonium carbonate to precipitate MnCO
3. The carbonate is
calcined in air to give a mixture of manganese(II) and manganese(IV) oxides. To complete the process, a suspension of this material in sulfuric acid is treated with
sodium chlorate.
Chloric acid, which forms in situ, converts any Mn(III) and Mn(II) oxides to the dioxide, releasing chlorine as a by-product.
[8]
Lastly, the action of potassium permanganate over manganese sulfate crystals produces the desired oxide. [9]
Electrolytic manganese dioxide (EMD) is used in zinc–carbon batteries together with zinc chloride and ammonium chloride. EMD is commonly used in zinc manganese dioxide rechargeable alkaline (Zn RAM) cells also. For these applications, purity is extremely important. EMD is produced in a similar fashion as electrolytic tough pitch (ETP) copper: The manganese dioxide is dissolved in sulfuric acid (sometimes mixed with manganese sulfate) and subjected to a current between two electrodes. The MnO2 dissolves, enters solution as the sulfate, and is deposited on the anode. [10]
The important reactions of MnO
2 are associated with its
redox, both oxidation and reduction.
MnO
2 is the principal
precursor to
ferromanganese and related alloys, which are widely used in the steel industry. The conversions involve
carbothermal reduction using
coke:
[11]
The key redox reactions of MnO
2 in batteries is the one-electron reduction:
MnO
2
catalyses several reactions that form O
2. In a classical laboratory demonstration, heating a mixture of
potassium chlorate and manganese dioxide produces oxygen gas. Manganese dioxide also catalyses the decomposition of
hydrogen peroxide to oxygen and
water:
Manganese dioxide decomposes above about 530 °C to
manganese(III) oxide and oxygen. At temperatures close to 1000 °C, the
mixed-valence compound Mn
3O
4 forms. Higher temperatures give MnO, which is reduced only with difficulty.
[11]
Hot concentrated
sulfuric acid reduces MnO
2 to
manganese(II) sulfate:
[4]
The reaction of
hydrogen chloride with MnO
2 was used by
Carl Wilhelm Scheele in the original isolation of
chlorine gas in 1774:
As a source of hydrogen chloride, Scheele treated sodium chloride with concentrated sulfuric acid. [4]
The
standard electrode potentials for the
half reactions indicate that the reaction is
endothermic at pH = 0 (1 M [H+
]), but it is favoured by the lower
pH as well as the evolution (and removal) of gaseous chlorine.
This reaction is also a convenient way to remove the manganese dioxide precipitate from the ground glass joints after running a reaction (for example, an oxidation with potassium permanganate).
Heating a mixture of
KOH and MnO
2 in air gives green
potassium manganate:
Potassium manganate is the precursor to potassium permanganate, a common oxidant.
The predominant application of MnO
2 is as a component of
dry cell batteries: alkaline batteries and so called
Leclanché cell, or
zinc–carbon batteries. Approximately 500,000
tonnes are consumed for this application annually.
[12] Other industrial applications include the use of MnO
2 as an inorganic
pigment in
ceramics and in
glassmaking. It is also used in water treatment applications.
[13]
Excavations at the Pech-de-l'Azé cave site in southwestern France have yielded blocks of manganese dioxide writing tools, which date back 50,000 years and have been attributed to Neanderthals . Scientists have conjectured that Neanderthals used this mineral for body decoration, but there are many other readily available minerals that are more suitable for that purpose. Heyes et al. (in 2016) determined that the manganese dioxide lowers the combustion temperatures for wood from above 650 °F to 480 °F, making fire making much easier and this is likely to be the purpose of the blocks. [14]
A specialized use of manganese dioxide is as oxidant in
organic synthesis.
[7] The effectiveness of the reagent depends on the method of preparation, a problem that is typical for other heterogeneous reagents where surface area, among other variables, is a significant factor.
[15] The mineral
pyrolusite makes a poor reagent. Usually, however, the reagent is generated in situ by treatment of an aqueous solution KMnO
4 with a Mn(II) salt, typically the sulfate. MnO
2 oxidizes
allylic alcohols to the corresponding
aldehydes or
ketones:
[16]
The configuration of the
double bond is conserved in the reaction. The corresponding
acetylenic alcohols are also suitable substrates, although the resulting
propargylic aldehydes can be quite reactive.
Benzylic and even unactivated alcohols are also good substrates. 1,2-
Diols are cleaved by MnO
2 to
dialdehydes or
diketones. Otherwise, the applications of MnO
2 are numerous, being applicable to many kinds of reactions including
amine oxidation, aromatization,
oxidative coupling, and
thiol oxidation.
In Geobacteraceae sp., MnO2 functions as an electron acceptor coupled to the oxidation of organic compounds. This theme has implications for bioremediation. [17]
{{
cite journal}}
: CS1 maint: multiple names: authors list (
link); Collected Volumes, vol. 9, p. 136. (this procedure illustrates the use of MnO2 for the oxidation of an allylic alcohol)
Names | |
---|---|
IUPAC names
Manganese dioxide
Manganese(IV) oxide | |
Other names
Pyrolusite, hyperoxide of manganese, black oxide of manganese, manganic oxide
| |
Identifiers | |
3D model (
JSmol)
|
|
ChEBI | |
ChemSpider | |
ECHA InfoCard | 100.013.821 |
EC Number |
|
PubChem
CID
|
|
RTECS number |
|
UNII | |
CompTox Dashboard (
EPA)
|
|
| |
| |
Properties | |
MnO 2 | |
Molar mass | 86.9368 g/mol |
Appearance | Brown-black solid |
Density | 5.026 g/cm3 |
Melting point | 535 °C (995 °F; 808 K) (decomposes) |
Insoluble | |
+2280.0×10−6 cm3/mol [1] | |
Structure [2] | |
Tetragonal, tP6, No. 136 | |
P42/mnm | |
a = 0.44008 nm, b = 0.44008 nm, c = 0.28745 nm
| |
Formula units (Z)
|
2 |
Thermochemistry [3] | |
Heat capacity (C)
|
54.1 J·mol−1·K−1 |
Std molar
entropy (S⦵298) |
53.1 J·mol−1·K−1 |
Std enthalpy of
formation (ΔfH⦵298) |
−520.0 kJ·mol−1 |
Gibbs free energy (ΔfG⦵)
|
−465.1 kJ·mol−1 |
Hazards | |
GHS labelling: | |
Warning | |
H302, H332 | |
P261, P264, P270, P271, P301+P312, P304+P312, P304+P340, P312, P330, P501 | |
NFPA 704 (fire diamond) | |
Flash point | 535 °C (995 °F; 808 K) |
Safety data sheet (SDS) | ICSC 0175 |
Related compounds | |
Other
anions
|
Manganese disulfide |
Other
cations
|
Technetium dioxide Rhenium dioxide |
Manganese(II) oxide Manganese(II,III) oxide Manganese(III) oxide Manganese heptoxide | |
Except where otherwise noted, data are given for materials in their
standard state (at 25 °C [77 °F], 100 kPa).
|
Manganese dioxide is the
inorganic compound with the
formula MnO
2. This blackish or brown solid occurs naturally as the mineral
pyrolusite, which is the main ore of
manganese and a component of
manganese nodules. The principal use for MnO
2 is for dry-cell
batteries, such as the
alkaline battery and the
zinc–carbon battery.
[4] MnO
2 is also used as a
pigment and as a precursor to other manganese compounds, such as
KMnO
4. It is used as a
reagent in
organic synthesis, for example, for the oxidation of
allylic
alcohols. MnO
2 has an α-
polymorph that can incorporate a variety of atoms (as well as water molecules) in the "tunnels" or "channels" between the manganese oxide octahedra. There is considerable interest in α-MnO
2 as a possible cathode for
lithium-ion batteries.
[5]
[6]
Several
polymorphs of MnO
2 are claimed, as well as a hydrated form. Like many other dioxides, MnO
2 crystallizes in the
rutile
crystal structure (this polymorph is called
pyrolusite or β-MnO
2), with three-coordinate oxide anions and octahedral metal centres.
[4] MnO
2 is characteristically
nonstoichiometric, being deficient in oxygen. The complicated
solid-state chemistry of this material is relevant to the lore of "freshly prepared" MnO
2 in
organic synthesis.
[7] The α-polymorph of MnO
2 has a very open structure with "channels", which can accommodate metal ions such as silver or barium. α-MnO
2 is often called
hollandite, after a closely related mineral.
Naturally occurring manganese dioxide contains impurities and a considerable amount of manganese(III) oxide. Production of batteries and ferrite (two of the primary uses of manganese dioxide) requires high purity manganese dioxide. Batteries require "electrolytic manganese dioxide" while ferrites require "chemical manganese dioxide". [8]
One method starts with natural manganese dioxide and converts it using
dinitrogen tetroxide and water to a
manganese(II) nitrate solution. Evaporation of the water leaves the crystalline nitrate salt. At temperatures of 400 °C, the salt decomposes, releasing N
2O
4 and leaving a residue of purified manganese dioxide.
[8] These two steps can be summarized as:
In another process, manganese dioxide is
carbothermically reduced to
manganese(II) oxide which is dissolved in
sulfuric acid. The filtered solution is treated with
ammonium carbonate to precipitate MnCO
3. The carbonate is
calcined in air to give a mixture of manganese(II) and manganese(IV) oxides. To complete the process, a suspension of this material in sulfuric acid is treated with
sodium chlorate.
Chloric acid, which forms in situ, converts any Mn(III) and Mn(II) oxides to the dioxide, releasing chlorine as a by-product.
[8]
Lastly, the action of potassium permanganate over manganese sulfate crystals produces the desired oxide. [9]
Electrolytic manganese dioxide (EMD) is used in zinc–carbon batteries together with zinc chloride and ammonium chloride. EMD is commonly used in zinc manganese dioxide rechargeable alkaline (Zn RAM) cells also. For these applications, purity is extremely important. EMD is produced in a similar fashion as electrolytic tough pitch (ETP) copper: The manganese dioxide is dissolved in sulfuric acid (sometimes mixed with manganese sulfate) and subjected to a current between two electrodes. The MnO2 dissolves, enters solution as the sulfate, and is deposited on the anode. [10]
The important reactions of MnO
2 are associated with its
redox, both oxidation and reduction.
MnO
2 is the principal
precursor to
ferromanganese and related alloys, which are widely used in the steel industry. The conversions involve
carbothermal reduction using
coke:
[11]
The key redox reactions of MnO
2 in batteries is the one-electron reduction:
MnO
2
catalyses several reactions that form O
2. In a classical laboratory demonstration, heating a mixture of
potassium chlorate and manganese dioxide produces oxygen gas. Manganese dioxide also catalyses the decomposition of
hydrogen peroxide to oxygen and
water:
Manganese dioxide decomposes above about 530 °C to
manganese(III) oxide and oxygen. At temperatures close to 1000 °C, the
mixed-valence compound Mn
3O
4 forms. Higher temperatures give MnO, which is reduced only with difficulty.
[11]
Hot concentrated
sulfuric acid reduces MnO
2 to
manganese(II) sulfate:
[4]
The reaction of
hydrogen chloride with MnO
2 was used by
Carl Wilhelm Scheele in the original isolation of
chlorine gas in 1774:
As a source of hydrogen chloride, Scheele treated sodium chloride with concentrated sulfuric acid. [4]
The
standard electrode potentials for the
half reactions indicate that the reaction is
endothermic at pH = 0 (1 M [H+
]), but it is favoured by the lower
pH as well as the evolution (and removal) of gaseous chlorine.
This reaction is also a convenient way to remove the manganese dioxide precipitate from the ground glass joints after running a reaction (for example, an oxidation with potassium permanganate).
Heating a mixture of
KOH and MnO
2 in air gives green
potassium manganate:
Potassium manganate is the precursor to potassium permanganate, a common oxidant.
The predominant application of MnO
2 is as a component of
dry cell batteries: alkaline batteries and so called
Leclanché cell, or
zinc–carbon batteries. Approximately 500,000
tonnes are consumed for this application annually.
[12] Other industrial applications include the use of MnO
2 as an inorganic
pigment in
ceramics and in
glassmaking. It is also used in water treatment applications.
[13]
Excavations at the Pech-de-l'Azé cave site in southwestern France have yielded blocks of manganese dioxide writing tools, which date back 50,000 years and have been attributed to Neanderthals . Scientists have conjectured that Neanderthals used this mineral for body decoration, but there are many other readily available minerals that are more suitable for that purpose. Heyes et al. (in 2016) determined that the manganese dioxide lowers the combustion temperatures for wood from above 650 °F to 480 °F, making fire making much easier and this is likely to be the purpose of the blocks. [14]
A specialized use of manganese dioxide is as oxidant in
organic synthesis.
[7] The effectiveness of the reagent depends on the method of preparation, a problem that is typical for other heterogeneous reagents where surface area, among other variables, is a significant factor.
[15] The mineral
pyrolusite makes a poor reagent. Usually, however, the reagent is generated in situ by treatment of an aqueous solution KMnO
4 with a Mn(II) salt, typically the sulfate. MnO
2 oxidizes
allylic alcohols to the corresponding
aldehydes or
ketones:
[16]
The configuration of the
double bond is conserved in the reaction. The corresponding
acetylenic alcohols are also suitable substrates, although the resulting
propargylic aldehydes can be quite reactive.
Benzylic and even unactivated alcohols are also good substrates. 1,2-
Diols are cleaved by MnO
2 to
dialdehydes or
diketones. Otherwise, the applications of MnO
2 are numerous, being applicable to many kinds of reactions including
amine oxidation, aromatization,
oxidative coupling, and
thiol oxidation.
In Geobacteraceae sp., MnO2 functions as an electron acceptor coupled to the oxidation of organic compounds. This theme has implications for bioremediation. [17]
{{
cite journal}}
: CS1 maint: multiple names: authors list (
link); Collected Volumes, vol. 9, p. 136. (this procedure illustrates the use of MnO2 for the oxidation of an allylic alcohol)